anodic coating

The colour of anodic coating is white and beautiful.

氧化膜颜色为白色，外观美丽。

To improve the anti-corrosion performance of electro coating inorganic inhibitors are applied in an anodic electrophoretic-coating.

在电泳涂装工艺中使用缓蚀剂,可提高阳极电泳涂层的 防 腐蚀性.

Electrolytic Coloring Anodic Coating of Al in a Bath Containning Cu and Ni Salts

阳极氧化铝在Cu-Ni混合浴中的电解着色

The aluminium is anodic coating to uranium, and offers sacrificial protection for uranium substrate. Sacrifice and Sacrificial poems

Al镀层相对U基体为阳极性镀层，能对U基体提供牺牲性保护；祖饯诗的由来

Causes of Aluminium Profile Anodic Coating Cracking and Preventive Measures

铝型材阳极氧化膜破裂原因及预防措施

White Anodic Coating on Aluminium Surface for Spacecraft

航天器用铝光亮阳极氧化涂层特性研究

Development of a Transparent Acrylic Anodic Electrophoretic Coating

透明丙烯酸阳极电泳涂料的研制

The change in current density during the electro-lytic colouring has been determined. The mechanism of AC electrolytic colouring of anodic coating on aluminum has been investigated according to the results of experiments mentioned above.

测定了交流电解着色过程中的电流密度变化，并根据以上实验结果，探讨了交流电解着色机理。

Studies on the Morphology, Structure and Composition of Anodic Oxide Coating on Aluminium and Its Alloy

铝阳极氧化膜的形态、结构和成分分布的研究

Determination of Solvents in Anodic Electrophoretic Coating by Gas Chromatography

气相色谱法测定阳极电泳涂料中溶剂含量

The result indicates that the coating grows in the following steps, i.e., the stage of anodic deposition, micro-arc oxidation and local arc light.

研究表明，微弧氧化过程可分为三个阶段，即：阳极沉积阶段、微弧阶段和局部弧光阶段；

Appropriate amount of Co_3O_4 will greatly enhance the catalytic activity of RuO_2-TiO_2 ( 60)/ Ti anode for chlorine evolution, and reduce the ohmic drop in anodic coating obviously.

适量Co3O4可以大大提高RuO2-TiO2（60）/Ti阳极的析氯催化活性，明显减小涂层欧姆降。

Tin-zinc alloy deposit is anodic coating to iron and steel.

锡锌合金镀层相对于钢铁基体为阳极性镀层。

General specification for anodic shield coating of ship and ocean engineering

GB/T7788-1987船舶及海洋工程阳极屏涂料通用技术条件

Wear Resistance Tests of Hard Anodic Coating on Aluminum Alloys

铝合金硬阳极化膜的耐磨试验

The Chromaticity of Electrolytic Colouring Anodic Coating of Aluminium and Its Alloys

铝及铝合金电解着色膜的色度研究

Preparation and Friction Behavior of Anodic Oxidation Coating on the Surface of Aluminum Alloy

铝合金表面阳极氧化膜的制备及其摩擦性能

Anodic coating is compact and uniform on the surface of samples after anodization.

微弧氧化后，氧化膜均匀、致密地生长在工件表面。

Electrolytic multi-coloring technique of anodic coating on aluminum

铝阳极氧化膜多色彩电解着色工艺

A new technology of electrolytic colouring for anodic coating of aluminium

阳极化铝电解着色新技术

The hardness of anodic oxidation layer is higher, the tribological property of composite coating is better.

阳极氧化层的硬度越大, 复合膜摩擦学性能越好.

In terms of the polarity of the electrodes acted by workpiece, the electrophoretic coating was divided into two kinds: anodic electrophoretic coating and cathodic electrophoretic coating.

根据被涂工件充当的电极性质，电泳涂料分为阳极电泳涂料和阴极电泳涂料。

Method for Repairing of Locally Damaged Anodic Oxidation Coating on Aluminum Alloy

铝合金阳极氧化膜局部破损的修复方法

Sealing of the Anodic Coating of Aluminium Alloy Used in Architecture

建筑用铝合金阳极氧化膜的封闭

Microstructures and Anticorrosion Behavior of Anodic Oxidized Coating on Al Alloy

2024铝合金阳极氧化膜的结构和耐蚀性能

The coloring process can be formed a complete set with anodic electrophoretic coating technology aluminium.

该着色工艺可和阳极电泳工艺配套.

Studies on Synthesis and Curing Behavior of Acrylic Anodic Electrophoretic Coating with High Hardness

高硬度丙烯酸阳极电泳涂料合成及固化特性研究

The feature, law and mechanism of6063aluminium profile anodic coating cracking exposed to the sunshine are studied.

研究了阳极氧化6063铝合金型材在曝晒时产生的氧化膜裂纹特征、规律及机理。

The morphology, structure and elemental composition distribution of anodic oxide coating on aluminium and its alloy are studied by means of TEM, SEM, AES and X-ray diffraction in this paper.

用TEM、SEM、AES和x射线衍射技术研究了铝阳极氧化膜的形态、结构和化学成分分布。

It has been de-termined by X-ray photoelectron spectroscopy ( XPS or ESCA) that the colou-ring material in pores of anodic coating on aluminum exists in the forms of tin metal and α-stannic acid.

用x光电子能谱法（XPS或ESCA）确定了着色物质是以金属锡和α锡酸的形式存在；